mujtank.cz

After I finished the casting of the upper part of the lower part of the form num.



Could I also this casting. The cap in the middle of the filling opening for the zinc.



After everything was nicely cured saw the moldings after separating from better.



But before I finished making the mold and still build with the vents , I'm still the master casts made ​​from resin . So I have the hassle with the shape is no longer relevant and the silicone can without much preliminary work direckt giesen on the master plates . The silicone mold will not even live forever.





The only drawback to this method is the rather large consumption of Resin, but it is still worthwhile if you need a new form .
Here you can see how pretty much the resin must be plate .



The same course I did that with the second mold half , only that I 've placed a displacement in the middle to save Resin .

Hi Edwin
Nice cake. It looks like a view into the kitchen.

Michal

Yes Zander,

only is the cake a very Tough and about the other one bites the teeth slightly from ....

Cheers, Edwin

Today I had again the time something to do here.

If I need now form a new centrifugal casting I can drain quickly with the Resin negative now.



In the right form now still missing, the vent holes. The I install with a 1mm drill at all relevant points.



Allow the air to escape during the casting and also the holes are not sealed by the pressure plate I milled with a cutting disc just still air channels through the holes.





Now I can soon try out the new form.

Today I finally tried my hand in rotational molding again .

First powdered forms .



Here you can see the difference as beautiful as the powder adhered to the silicone.



Place the brass tubes for the pin bearing into the mold.



And close the mold and screw it into the skid pan .



After I had melted enough zinc , I could pour it into the opening.



The first pour but has become anything yet. The speed was too high and not pressed the mold enough to each other. As a part of the zinc is ejected from the From and only two of the six members are useful . I think the temperature of the zinc was too hot .







So the same again and this . Sometimes with less temperature and lower speed This was but now back to low. The casting looks good, but the form is not completed and the parts so flawed .



That will probably still be some work until it works to my satisfaction.

After a few small changes it went today. I do but only piece by piece and so I first have installed a few vents .







It has gotten better , but I see the need again to make a new form and I also do not know if I need a slightly harder silicone for this, as some slightly bent chain links come from the mold. On the second cast I had way too little material which is why two of the forms were not filled sufficiently . What I do not like is the surface of the chain. That was much better from the single form.

So now I have at least some members whose quality is just sufficient for use according to my understanding . Therefore, I have now started with the assembly of which is still a lot of work .

First, disconnect the small brass tubes with a band saw , as far as you can reach it .



The pipe pieces that you can not cut so I have to cut out with a small blade.



Then I can edit the links with a small belt sander .



When connecting bolts I use 2mm spring steel. It is so stable that 150kg train at enem piece of chain had led to no deformation or tearing .



And here , the combined length of chain . The slightly shorter is still the tensile test , but it can recognize the much better surface. The temperature of the mold makes the way, since no difference.
In the foreground is a small piece of 1/16 chain as a comparison.

By the way I bring it to me, too just 3D CAD with and just created a caster in 3D for it to be able to create master.

It's times as one half of a roller in 1/6

I am still on the accumulation of experience , but as a little I get on.

Having trouble by default and surface in rotational molding I have by the shape and size of the chain links , but I learned a lot again, I 'm working around a bit on my last microframe form. Since I will build such a form anyway also my past experience again, I can I still edit these a little and see what happens and lo and behold ....

With the reworked form I was able to immediately resolve 90 % of the remaining problems. Delay and poor surface I had not at this silicone anyway. Just filling out the form I had not yet under control.

Now only two places that I also already have almost the handle is missing .







I'll be there now try around a little and then build a new form of the current experience .

Before I can build a new form with which I can implement my previous experience I will create a larger and more flexible molded frame.

This I 'm from 11.5 mm Alunminium
rods which I abfräse at the ends and in the middle , and thrust . So I can put together any bars like a log cabin .
Because the whole is built of nothing but remnants , it does not look professional, but serves its purpose. So I can now shapes in different sizes presses. The framework I have made ​​it so big that it still fits well in my small oven.



After the frame is ready , I can the new form, which is slightly larger than my old frame zulies .
Thus, the silicone not verklezt with the frame I Dress him first with baking paper . Since I do not need the whole form I use old silicone molds as filling klotz



So , I offer two silicon plates and press the Master in the silicone.



As Trennmttel I dove all a with talc and as a connector I use self- cast knobs .

[ mg] ttp://up.picr.de/17396627av.jpg[/img]

So I can then rebuild the shape of three parts in one whole ..

After all silicone is processed I 'm still a chunk of aluminum to press it and screw the cover plate of the mold .
This I will still be a few minutes and put the screws again somewhat, because the silicone deforms as a viscous mass .





I put the oven on the terrace , because the smell in enclosed spaces is not exactly edifying , and make the form now by 1.5 hours.



Then I just have to cut the sprues and can use the form immediately.

After the mold was allowed to overnight, unpacking was first time announced.



After I had the shape plastered around something . It has pushed the silicone into each hole . I had to separate the mold , which is not easy. But if you have found the beginning , it is no longer a problem .



The next step was to cut the sprues with a carving knife into the silicone. This works simply because it is quite stable and stiff.



After I had installed a couple of vent holes and the shape well dusted with talc , it went to the first casting.





But a little rework was required.
But now I have the alues ​​form come from the useful links and that I can use .



The rework is almost consuming than the preparation and casting itself so you have to grind a lot , including the little hand belt sander proven once again very good.



After cutting out the Messingröchen I could start the first chain links with a 2mm spring steel bolts to connect.





What I notice when casting to my surprise is that the cold mold works best. If this is too warm arise all of a sudden again cavities and the cast is not usable.

Now I 'm going to make these chain links two new master and from two new forms that will be even better. So then the production of the chains begin for the prototypes.